How you get on Tussock?
Sent from my GT-I9300T using Tapatalk 2
Type: Posts; User: tui_man2
How you get on Tussock?
Sent from my GT-I9300T using Tapatalk 2
Be good to see how they come up, you going to do the lot or do a batch and test them?
Here's some more I'm doing at moment have 300 down 200 to go, then the forming of shoulder forward. The ones...
It works mate an will extend you life of brass. but past 4-500m expect fliers an erratic groups with un even neck tension, is what im meaning.
Its easy to do, i would happy do it but wont be for...
Even heat, even time, so they are all the same an even given if you have it a little differnt each time in set up etc it wont matter if you do it as a batch.
Doing it by hand you can be dirrerent...
Some that I have started for a mate 6.5 284 fired 4 times left, cleaned, annealed an neck sized right.
It's by all means easy to do by hand but if you want neck tensions right for out a wee way...
Like you in most cases its the easier way to be when its getting say get new brass
Only odd ball cases make it really worth while an in the forming stages
So you would rather anneal the whole case? That's why you don't need to do it. Or all your brass will be going to the scrap man:rolleyes:
Sent from my GT-I9300T using Tapatalk 2
Still has error but if not shooting far then it wont matter anyway.
Lapua is as good as it gets an it comes annealed ready to load
Doing it by had is to hit an miss
I have made an are making...
I know that I was meaning there is no half arsed way. Either do it right all timed the same or don't do it all all. Neck tension will be all different from case to case by hand so may as well not...
Because why you can do it yourself they will be all inconsistent so may as well not even do it. Unless you have odd ball cals that you have to fire form or form in forming dies its not worth the...