The important thing to remember is that the important thing is they are all the same, if your method is at all variable annealing at a high temperature will remove most variation in hardness and...
Type: Posts; User: veitnamcam
The important thing to remember is that the important thing is they are all the same, if your method is at all variable annealing at a high temperature will remove most variation in hardness and...
Bite the neck, you will soon tell the difference between annealed and fully work hardened, its to soft when it collapses in your die and its too hot when it looses all shine.
While I have not tried that method personally it has its merits and draw backs.
Primer in, the air heating inside the case will push the moulton lead out as pressure rises keeping hopefully the...
The only reason to quench is if your heat source is that pathetic it takes so long to get the neck and shoulder up to temp it is heating the case way back into the body or web, you definitely DO NOT...
That looks very dairy farmer but lets face it we are not launching a space shuttle to start human civilisation on another planet, looks like it will do the job asked of it and I look forward to...
This graph from TeReis link shows what I was trying to explain earlier with my over annealing by hand comment.
32329
As you can see if you are heating by hand and you are only just getting into...
Kiwi Greg s machine is quick and consistent, I think if you "over anneal" then you will have less inconsistency doing it by hand but this may not be any better and maybe worse for brass life if the...
I found it essential for any kind of consistency running subsonic .308
I would just do the same as you on my portable bbq but for subsonic I would "over anneal" it so was soft as in the neck, if un...