Other way round, quench them to make the brass soft. If it was just air cool then you would never need to do it as that would be the same as firing and letting the brass cool naturally.
Type: Posts; User: Wirehunt
Other way round, quench them to make the brass soft. If it was just air cool then you would never need to do it as that would be the same as firing and letting the brass cool naturally.
You answered your own question here. PMC. Shit. Unless something amazing has happened it's never been good brass.