oh man can I now relate to that comment.....
Type: Posts; User: Micky Duck
oh man can I now relate to that comment.....
anyone else notice how cracked edge is blackened??? not what I would expect from a fresh break at all
Ive NEVER annealed.....have some .270 brass with maybe dozen loads through them...Ive seen case seperation down in web area ,also seen it in .223 but never what you have shown....at all.